Effect of Additional Dry Heat Curing on Microflexural Strength in Three Types of Resin Composite: An In Vitro Study
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Authors
Zamalloa-Quintana, MarlonLópez-Gurreonero, Carlos
Santander-Rengifo, Flor Magaly
Ladera-Castañeda, Marysela
Castro-Pérez Vargas, Antonieta
Cornejo-Pinto, Alberto
Cervantes-Ganoza, Luis
Cayo-Rojas, César
Issue Date
2022-08-01Keywords
complementary polymerizationdentistry
heat treatment
mechanical properties
microflexural strength
resin composite
Metadata
Show full item recordPublisher
MDPIJournal
CrystalsDOI
10.3390/cryst12081045Additional Links
https://www.mdpi.com/2073-4352/12/8/1045Abstract
Aim: Additional dry heat curing is a method that favorably influences the mechanical properties of an indirect resin composite restoration. Microflexural strength is a property currently applied for the evaluation of indirect resin composite restorations. The aim of the present study was to assess the effect of additional dry heat curing on microflexural strength in three types of direct-use resin composites. Materials and Methods: This in vitro study consisted of 70 resin composites samples made with a 6 × 2 × 1 mm metal matrix and divided into seven experimental groups, which included Gr1a: Tetric N-Ceram without additional dry heat curing (n = 10); Gr1b: Tetric N-Ceram with additional dry heat curing (n = 10); Gr 2a: Filtek Z350 XT without additional dry heat curing (n = 10); Gr2b: Filtek Z350 XT with additional dry heat curing (n = 10); Gr3a: Filtek Z250 without additional dry heat curing (n = 10); Gr3b: Filtek Z250 with additional dry heat curing (n = 10); and Gr4: SR Nexco Paste (control) without additional dry heat curing (n = 10). The samples were stored in distilled water at 37 °C for 24 h. A universal testing machine with a 2000 N load cell at a speed of 1 mm/min was used to assess flexural strength. The data were analyzed with a parametric ANOVA test with Tukey’s post hoc intergroup factor (for groups without heat treatment) and a nonparametric Kruskall Wallis test with Bonferroni’s post hoc (for groups with heat treatment). In addition, the comparison of independent groups in each resin composite type with and without heat treatment was performed with a Mann Whitney U test. A significance level of p < 0.05 was considered. Results: The Filtek Z250 resin composite with and without additional dry heat curing presented the highest microflexural strength values with 137.27 ± 24.43 MPa and 121.32 ± 9.74 MPa, respectively, while the SR Nexco Paste (control) resin composite presented the lowest microflexural strength values with 86.06 ± 14.34 MPa compared to all the resin composites with additional dry heat curing. The Filtek Z250 and Filtek Z350XT resin composites with and without additional dry heat curing presented significantly higher microflexural strength versus the SR Nexco (p < 0.05) and Tetric N-Ceram (p < 0.05) resin composites. In addition, the Filtek Z350XT and Tetric N-Ceram resin composites with additional dry heat curing showed significantly higher microflexural strength (p < 0.05) compared to those without additional dry heat curing. Conclusions: The Filtek Z250 and Z350XT resin composites had significantly higher microflexural strength values with and without additional dry heat curing. In addition, the Filtek Z350XT and Tetric N-Ceram resin composites subjected to additional dry heat curing showed significantly higher microflexural strength compared to when they did not receive the same procedure, a situation that did not occur with the Filtek Z250 resin composite.Type
info:eu-repo/semantics/articleRights
Attribution-NonCommercial-ShareAlike 4.0 InternationalLanguage
engEISSN
20734352ae974a485f413a2113503eed53cd6c53
10.3390/cryst12081045
Scopus Count
Collections
The following license files are associated with this item:
- Creative Commons
Except where otherwise noted, this item's license is described as Attribution-NonCommercial-ShareAlike 4.0 International