Propuesta de uso de cenizas de cáscara de arroz y fibras de polipropileno en diseños de mezclas de concreto para el control de fisuras en losas macizas entrepiso in-situ en la ciudad de Lima
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Issue Date
2020-11-30Keywords
Ceniza de cáscara de arrozFibra de polipropileno
Fisuras
Losas
Resistencia a la compresión
Resistencia a la flexión
Rice husk ash
Polypropylene fiber
Slump
Compressive strength
Flexural strength
Metadata
Show full item recordOther Titles
Proposal for the use of rice husk ash and polypropylene fibers in concrete mix designs for the control of cracking in concrete structures in the city of LimaAbstract
La presente investigación fue elaborada con el fin de estudiar la influencia que tiene el agregar cenizas de cascara de arroz (CCA) y fibras de polipropileno (FPP) en la fisuración por contracción plástica del concreto. El estudio de investigación tuvo lugar en la ciudad de Lima, donde nos enfocamos a investigar las propiedades plásticas y mecánicas de un concreto f´c=210 kg/cm2, que se utiliza comúnmente en la fabricación de losas macizas, con reemplazo parcial del cemento por CCA en porcentajes de 5%, 10% y 15% respecto a su peso, y FPP en rendimiento de 900 gr/m3. Las principales propiedades en estado endurecido fueron investigadas, la resistencia a la compresión y la resistencia a la flexión y la propiedad en estado plástico que se desarrolló fue la fisuración debido a la contracción plástica a través del ensayo ASTM C1579. Teniendo en cuenta que no existe un acuerdo relativo al ancho de fisura máxima en un elemento estructural, se decidió utilizar límites entre 0.2 a 0.4 mm, para ambientes normales, sugeridos por el Mg. Ing. Gianfranco Ottazzi. De los resultados obtenidos, la mezcla adicionada con CCA en reemplazo parcial del cemento en 5%, 10% y 15% junto con las FPP en rendimiento de 900 gr/m3, podemos inferir que las CCA reducirán, no de manera significativa, las propiedades de la resistencia de un concreto f´c= 210 kg/cm2, sin embargo, reducen el promedio de apariciones de fisuras producidas en las losas macizas debido la contracción plástica del mismo.The present investigation was elaborated with the purpose of studying the influence of the addition of rice husk ash (RHA) and polypropylene fibers (PPF) on the plastic shrinkage cracking of concrete. The research study took place in the city of Lima, where we focused on investigating the plastic and mechanical properties of a concrete f´c = 210 kg / cm2, which is commonly used in the manufacture of solid slabs, with partial replacement of the cement by RHA in percentages of 5%, 10% and 15% respect to its weight and PPF in yield of 900 g / m3. The main properties in the hardened state were investigated, the compressive strength and flexural strength and the property in the plastic state that developed was cracking due to plastic shrinkage through the ASTM C1579 test. Taking into account that there is no agreement regarding the maximum width in a structural element, it was decided to use limits between 0.2 to 0.4 mm, for normal environments, suggested by Mg. Eng. Gianfranco Ottazzi. According to the results obtained, the mixture added with RHA in replacement of cement in percentages of 5%, 10% and 15% together with PPF in yield of 900 gr / m3, we can infer that the RHA will reduce, not significantly, the strength properties of a concrete f´c = 210 kg / cm2, however, reduce the average occurrence of cracks produced in solid slabs due to the plastic shrinkage of the same.
Type
info:eu-repo/semantics/bachelorThesisRights
info:eu-repo/semantics/openAccessAttribution-NonCommercial-ShareAlike 4.0 International
Language
spaCollections
The following license files are associated with this item:
- Creative Commons