Evaluación in vitro de la Rugosidad Superficial de una pasta experimental de pulido para acrílico a base de conchas de moluscos
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Fecha de publicación
2020-07-08Palabras clave
Rugosidad superficialAcrílico dental
Pulido dental
Conchas de moluscos
Surface roughness
Dental acrylic
Dental polish
Seashells
Metadatos
Mostrar el registro completo del ítemOtros títulos
In vitro Evaluation of the surface roughness of an experimental polishing paste for acrylic based on seashellsResumen
Objetivo: Evaluar in vitro la rugosidad superficial de una pasta experimental de pulido para acrílico a base de conchas de moluscos. Materiales y métodos: Un total de 74 especímenes de acrílico fueron divididos en 2 grupos (n=37). Todos los especímenes fueron confeccionados con una matriz metálica (14x5x6 mm) y pulidos con una pasta experimental a base de Donax Obesulus y piedra pómez con un tamaño de partículas de 15µm, respectivamente para cada grupo. La rugosidad superficial inicial y final fue evaluada con un rugosímetro luego del pulido de los especímenes. Los datos fueron analizados mediante estadística descriptiva (media, mediana, desviación estándar y rango intercuartílico) e inferencial (Prueba de Wilcoxon pareada y Prueba de U de Mann Whitney) (p<0.05). Resultados: Los especímenes pulidos con piedra pómez mostraron mayores valores de rugosidad (0,45±0,12 µm); mientras que los especímenes que fueron pulidos con la pasta experimental tuvieron menores valores de rugosidad (0,50±0,07µm). Pese a ello, no se encontró diferencia estadísticamente significativa entre la rugosidad superficial de la pasta experimental y el grupo control (p = 0.309). Conclusiones: La pasta experimental a base de conchas de moluscos redujo los valores de rugosidad superficial en las superficies del acrílico dental.Objective: To evaluate in vitro the surface roughness of an experimental polishing paste for acrylic based on seashells. Materials and methods: A total of 74 acrylic specimens were divided into 2 groups (n = 37). All specimens were made with a metal matrix (14x5x6 mm) and then polished with an experimental paste and pumice stone with a particle size of 15 µm, respectively for each group. Initial and final surface roughness was evaluated after polishing the specimens. The data were analyzed using descriptive (mean, median, standard deviation and interquartile range) and inferential statistics (Wilcoxon signed-rank test and Mann Whitney U test) (p<0.05). Results: Specimens polished with pumice had higher roughness values (0.16 ± 0.06 µm), whereas specimens polished with the seashell powder had lower values in their surface roughness (0.09 ± 0.03 µm). Despite this, no statistically significant difference was found between the surface roughness of the experimental paste and the control group (p = 0.309). Conclusions: The experimental paste made of seashells reduced the surface roughness values on dental acrylic surface.
Derechos
Attribution-NonCommercial-ShareAlike 4.0 Internationalinfo:eu-repo/semantics/openAccess
Descripción
Rugosidad superficial, acrílico dental, pulido dental, conchas de moluscos. Surface roughness, dental acrylic, dental polish, seashells.Colecciones
El ítem tiene asociados los siguientes ficheros de licencia:
- Creative Commons
Excepto si se señala otra cosa, la licencia del ítem se describe como Attribution-NonCommercial-ShareAlike 4.0 International