Comparación in vitro de la microdureza y rugosidad del cerómero antes y después de su exposición a una bebida energizante
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Fecha de publicación
2020-01-29Palabras clave
Bebidas energéticasPruebas de dureza
Rugosidad
Cerómero
Energy drinks
Hardness tests
Roughness
Ceromer
Metadatos
Mostrar el registro completo del ítemResumen
Objetivo: Comparar in vitro la microdureza y rugosidad superficial del cerómero antes y después de su exposición a una bebida energizante. Materiales y métodos: Este estudio fue de tipo experimental in vitro. Se evaluaron 20 discos tipo cilíndricos (6 mm de altura y 4 mm de ancho) del cerómero SR Adoro® divididos en dos grupos para evaluar la microdureza superficial y rugosidad superficial. El desafío erosivo se realizó por 30 minutos/1 vez/ 5 días con la bebida Red Bull®. El análisis estadístico que se utilizó para evaluar la microdureza superficial fue la prueba de Wilcoxon. Sin embargo, para evaluar la rugosidad superficial se utilizó la prueba de T Student. Resultados: Se encontraron diferencias estadísticamente significativas al evaluar la microdureza superficial. Sin embargo, no se encontraron diferencias significativas al evaluar la rugosidad superficial del cerómero. La media y desviación estándar de la microdureza superficial del cerómero SR Adoro® antes del desafío erosivo fue de 55.45 + 6.42 MPa y después del desafío erosivo fue de 38.24 + 6.09 MPa. La diferencia de microdureza superficial inicial y final fue de 17.21+ 0.33 MPa. La media y desviación estándar de la rugosidad del cerómero SR Adoro® antes del desafío erosivo fue de 1.66 + 0.30 y después fue de 1.703 + 0.43 µm. La diferencia de rugosidad inicial y final del cerómero SR Adoro® expuesta a la bebida (Red Bull®) fue de 0.04+ 0.33 µm. Conclusiones: Existen diferencias estadísticamente significativas al evaluar la microdureza superficial. Sin embargo, no se encontraron diferencias estadísticamente significativas al evaluar la rugosidad del cerómero SR Adoro® (p<0.05; p=0.808) al ser expuesta a una bebida energizante Red Bull®.Objective: To compare in vitro the superficial microhardness and roughness of the ceromer before and after being exposed to an energizing drink. Materials and methods: This study was of experimental type in vitro. Twenty cylindrical discs (6 mm high and 4 mm wide) of the SR Adoro® ceromer were divided into two groups to evaluate the surface microhardness and surface roughness. The erosive challenge was performed for 30 minutes / 1 time / 5 days with the Red Bull® drink. The statistical analysis that was used to evaluate the surface microhardness was the Wilcoxon test. However, the Student's T test was used to evaluate the surface roughness. Results: Statistically significant differences were found when evaluating surface microhardness. However, no significant differences were found when evaluating the roughness of the ceromer. The mean and standard deviation of the surface microhardness of the SR Adoro® ceromer before the erosive challenge was 55.45 + 6.42 MPa and after the erosive challenge was 38.24 + 6.09 MPa. The difference of initial and final surface microhardness was 17.21 + 0.33 µm. The mean and standard deviation of the rugosity of the SR Adoro® ceromer before the erosive challenge was 1.66 + 0.30 µm and then was 1.703 + 0.43 µm. The initial and final roughness difference of the SR Adoro® ceromer exposed to the beverage (Red Bull®) was 0.04 + 0.33 µm. Conclusions: There are statistically significant differences when evaluating surface microhardness. However, no statistically significant differences were found when assessing the rugosity of the SR Adoro® ceromer (p<0.05, p = 0.808) when exposed to a Red Bull® energy drink.
Tipo
info:eu-repo/semantics/bachelorThesisDerechos
info:eu-repo/semantics/openAccessAttribution-NonCommercial-ShareAlike 4.0 International
Idioma
spaColecciones
El ítem tiene asociados los siguientes ficheros de licencia:
- Creative Commons
Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess