Evaluación in vitro de la microrugosidad superficial de dos resinas tipo Bulk Fill inmersas a dos bebidas rehidratantes con pH de 2,79 y 3,3
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Authors
Avila Solis, Sandra MilagrosAdvisors
Hermoza Novoa, Mónica MercedesIssue Date
2019-10-21
Metadata
Show full item recordOther Titles
In vitro comparison of superficial microroughness of two Bulk Fill resins composites inmersed into two soft drinksCitation
1. Avila Solis, SM. Evaluación in vitro de la microrugosidad superficial de dos resinas tipo Bulk Fill inmersas a dos bebidas rehidratantes con pH de 2,79 y 3,3 [Internet]. [Lima, Perú]: Universidad Peruana de Ciencias Aplicadas(UPC).; 2019. Disponible en: http://hdl.handle.net/10757/628127Abstract
Objetivo: Comparar in vitro la rugosidad superficial de una resina compuesta tipo BulkFill: Aura® BulkFill (SDI) con la resina Tetric N-Ceram® BulkFill (Ivoclar Vivadent) al ser inmersas a dos bebidas rehidratantes: Sporade® y Gatorade®. Materiales y métodos: Se utilizaron 88 especímenes de resina divididos en cuatro grupos, confeccionados con una matriz metálica (10mm x 4mm). Se insertó las resinas con una espátula de resina, y se fotoactivó con la lámpara Elipar LedTM, con una intensidad de 1200 mW/cm2. Se sumergieron los especímenes en agua destilada. A las 24 horas, se midió la rugosidad con el rugosímetro Mitutoyo SJ-210P. Luego, se realizó la inmersión en bebidas rehidratantes y se midió la rugosidad final a los 7 días. Resultados: La rugosidad inicial y final de las resinas Aura® BulkFill (SDI) y Tetric N-Ceram® BulkFill (Ivoclar Vivadent) presentaron diferencias significativas después de la inmersión en bebidas rehidratantes. Para los especímenes de Aura® BulkFill (SDI) al someterla a Sporade® se encontró una media inicial de 1.20 y una media final de 1.76 y los valores para Gatorade® fueron 0.77 y 1.73. Mientras que la rugosidad superficial de Tetric N-Ceram® BulkFill (Ivoclar Vivadent) al sumergirla en Sporade® fue 0.82 y 1.55, y en Gatorade® 0.77 y 1.73. Al comparar la diferencia de la rugosidad superficial final e inicial (deltas), la resina Aura® BulkFill presentó diferencias significativas mientras que, Tetric N-Ceram® BulkFill no tuvo diferencias al sumergirlas en ambas bebidas rehidratantes. Conclusiones: Las resinas estudiadas incrementaron su rugosidad luego de ser inmersas a las bebidas mencionadas.Objective: To compare in vitro the surface roughness of a BulkFill composite resin: Aura® BulkFill (SDI) with Tetric N-Ceram® BulkFill resin (Ivoclar Vivadent) when immersed in two rehydration drinks: Sporade® and Gatorade®. Materials and methods: 88 resin specimens divided into four groups were used, with a metal matrix (10 mm x 4 mm). The resins were inserted with a resin spatula, and photo-activated with the Elipar LedTM lamp, with an intensity of 1200 mW/cm2. The specimens were immersed in distilled water. After 24 hours, the roughness was measured with the Mitutoyo SJ-210P rugosimeter. Then, the immersion in rehydration drinks was performed and the final roughness was measured after 7 days. Results: The initial and final roughness of the resins Aura® BulkFill (SDI) and Tetric N-Ceram® BulkFill (Ivoclar Vivadent) showed significant differences after immersion in rehydration drinks. For specimens of Aura® BulkFill (SDI) when subjected to Sporade® an initial mean of 1.20 and a final average of 1.76 was found and the values for Gatorade® were 0.77 and 1.73. While the surface roughness of Tetric N-Ceram® BulkFill (Ivoclar Vivadent) when immersed in Sporade® was 0.82 and 1.55, and in Gatorade® 0.77 and 1.73. When comparing the difference of the final and initial surface roughness (deltas), the Aura® BulkFill resin showed significant differences while, Tetric N-Ceram® BulkFill did not have differences when immersing them in both rehydration drinks. Conclusions: The resins studied increased their roughness after being immersed in the aforementioned beverages.
Type
info:eu-repo/semantics/bachelorThesisRights
info:eu-repo/semantics/openAccessAttribution-NonCommercial-ShareAlike 4.0 International
Language
spaCollections
The following license files are associated with this item:
- Creative Commons