dc.identifier.citation1. Farfán B, Elizabeth N, Livias L, Danilo O. Comparación in vitro de la resistencia a la compresión y resistencia flexural de resinas Bulk Fill (OpusTM Bulk Fill, Tetric® N-Ceram Bulk Fill y FiltekTM Bulk Fill) [Internet]. [Lima, Perú]: Universidad Peruana de Ciencias Aplicadas(UPC).; 2018. Available from: http://hdl.handle.net/10757/624900es_PE
dc.identifier.doi10.19083/tesis/624900es_PE
dc.identifier.urihttp://hdl.handle.net/10757/624900
dc.description.abstractObjetivo: Comparar in vitro la resistencia a la compresión y resistencia flexural de resinas Bulk Fill (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill) Materiales y métodos: Se confeccionaron 132 especímenes en total: G1/G5: Opus™ Bulk Fill, G2/G6: Tetric® N-Ceram Bulk Fill, G3/G7: FiltekTM Bulk Fill y G4/G8: FiltekTM Z350XT (grupo control). Cincuenta y seis especímenes cilíndricos (3x5mm) para evaluar la resistencia a la compresión, divididos en 4 grupos (n=14): G1, G2, G3 y G4 y setenta y seis especímenes rectangulares para evaluar la resistencia flexural, divididos en 4 grupos (n=19): G5, G6, G7 y G8. Las pruebas mecánicas se realizaron en una máquina de ensayo universal Instron® con una carga de 100kN a 1mm/1min (Resistencia Compresiva) y una velocidad de 1mm/1min (Resistencia Flexural). El análisis de datos se realizó mediante estadística descriptiva e inferencial (test de Kruskal Wallis /prueba post hoc). Resultados: Para la resistencia a la compresión, los resultados fueron: G1 (141.68 MPa ± 22.20), G2 (139.03 MPa ± 23.56), G3 (235.59 MPa ± 26.08) y G4 (99.28 MPa±11.36). Se encontró diferencias estadísticamente significativas entre todas las resinas evaluadas (p<0.001). Para resistencia flexural los resultados fueron: G5 (116.29 MPa ± 7.20), G6 (109.67 MPa ± 7.58), G7 (200.53 MPa ± 10.32) y G8 (90.08 MPa ± 8.63). Se encontró diferencias estadísticamente significativas entre todas las resinas evaluada (p<0.001). Conclusiones: La resina Filtek™ Bulk Fill presentó mayor resistencia a la compresión y flexural en relación a las resinas evaluadas.en_US
dc.description.abstractObjective: Compare in vitro the compressive strength and flexural strength of Bulk fill resin composite (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill). Method and materials: 132 specimens were made: G1/G5: Opus™ Bulk Fill, G2/G6: Tetric® N-Ceram Bulk Fill, G3/G7: FiltekTM Bulk Fill y G4/G8: FiltekTM Z350XT (control group). Fifty-six cylindrical samples (3x5mm) to evaluate the compressive strength, divided in 4 groups (n=14): G1, G2, G3 y G4 and seventy-six rectangular samples to evaluate flexural strength, divided in 4 groups (n=19): G5, G6, G7 y G8. The mechanical tests were made with the Instron® Universal Testing Machine at crosshead speed of 1.0 mm/min with a load of 100 kN to compressive strength and at crosshead speed of 1.0 mm/min to flexural strength. The data analysis was performed by descriptive and inferential statistics (test de Kruskal Wallis /test post hoc). Results: For the compressive strength, the results were: G1 (141.68 MPa± 22.20), G2 (139.03 MPa ± 23.56), G3 (235.59 MPa ± 26.08) y G4 (99.28MPa±11.36). Statistically significant differences were found between all the groups (p> 0.001). For flexural strength the results were: G5 (116.29MPa ± 7.20), G6 (109.67 MPa ± 7.58), G7 (200.53 MPa ± 10.32) y G8 (90.08 MPa ±8.63). Statistically significant differences were found between all the groups (p> 0.001). Conclusion: Filtek ™ Bulk Fill resin composite showed greater compressive and flexural strength in comparison to the other resins evaluated.en_US
dc.description.uriTesises_PE
dc.formatapplication/pdfen_US
dc.formatapplication/epuben_US
dc.formatapplication/msworden_US
dc.language.isospaen_US
dc.publisherUniversidad Peruana de Ciencias Aplicadas (UPC)en_US
dc.rightsinfo:eu-repo/semantics/embargoedAccessen_US
dc.rightsAttribution-NonCommercial-ShareAlike 3.0 United States*
dc.rights.urihttp://creativecommons.org/licenses/by-nc-sa/3.0/us/*
dc.sourceUniversidad Peruana de Ciencias Aplicadas (UPC)es_PE
dc.sourceRepositorio Académico - UPCes_PE
dc.subjectCementos de resinaen_US
dc.subjectResinas compuestasen_US
dc.subjectPruebas de durezaen_US
dc.subjectOdontologíaen_US
dc.titleComparación in vitro de la resistencia a la compresión y resistencia flexural de resinas Bulk Fill (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill)en_US
dc.title.alternativeIn vitro comparison of the compressive strength and flexural strength of Bulk Fill resin composite (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y FiltekTM Bulk Fill).en_US
dc.typeinfo:eu-repo/semantics/bachelorThesisen_US
thesis.degree.grantorUniversidad Peruana de Ciencias Aplicadas (UPC). Facultad de Ciencias de la Saludes_PE
thesis.degree.levelLicenciaturaes_PE
thesis.degree.disciplineOdontologíaes_PE
thesis.degree.nameCirujano dentistaes_PE
refterms.dateFOA2019-01-16T20:02:46Z
dc.identifier.isni0000 0001 2196 144X


Files in this item

Thumbnail
Name:
borja_fn loyola_ld.pdf
Size:
554.8Kb
Format:
PDF
Thumbnail
Name:
borja_fn loyola_ld.docx
Embargo:
2088-12-05
Size:
690.2Kb
Format:
Microsoft Word 2007
Thumbnail
Name:
borja_fn loyola_ld.Ficha.pdf
Size:
77.08Kb
Format:
PDF

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/embargoedAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/embargoedAccess