Mejoramiento de la resistencia a compresión y flexión de concreto sostenible a elevadas temperaturas, con adición de cenizas puzolánicas
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Asesores
Carrera Cabrera, Elsa CarmenFecha de publicación
2021-08-21Palabras clave
Cenizas de cascara de arrozResistencia a compresión
Resistencia a flexión
Rice husk ashes
Compressive strength
Flexural strength
Metadatos
Mostrar el registro completo del ítemOtros títulos
Improvement of the compressive and flexural strength of sustainable concrete at elevated temperatures, with the addition of pozzolanic ashResumen
El presente artículo de estudio analizó la resistencia al fuego del concreto con adición de cenizas de cascara de arroz (CCA) y bagazo de caña de azúcar (CBCA). Se adoptó un método experimental como diseño de investigación, que produjo setenta y dos probetas cilíndricas (72) y cincuenta y cuatro vigas (54), para ensayos a compresión y flexión respectivamente. Se utilizaron cenizas en porcentajes de 5% y 10% y además una combinación binaria de 5% y 5% de ambas cenizas como reemplazo parcial de cemento. Las muestras fueron ensayadas luego de 28 días de curado a temperaturas de 24 °C (ambiente), 300 °C y 500 °C, con una duración de 2h de exposición y luego de 24 horas de enfriamiento al aire libre. Los resultados muestran un aumento de resistencia promedio a la compresión y flexión de hasta un 95% y 25%, respectivamente, luego de ser expuestos a temperaturas elevadas con respecto a las muestras de control.This study article analyzed the fire resistance of concrete with the addition of rice hull ash (CCA) and sugarcane bagasse (CBCA). An experimental method was adopted as the research design, which produced seventy-two cylindrical specimens (72) and fifty-four beams (54), for compression and bending tests respectively. Ashes were used in percentages of 5% and 10% and a binary combination of 5% and 5% of both ashes as a partial replacement for cement. The samples were tested after 28 days of curing at temperatures of 25 ° C (ambient), 300 ° C and 500 ° C, with a duration of 2 hours of exposure and after 24 hours of cooling in the open air. The results show an increase in average resistance to compression and flexion of up to 95% and 25%, respectively, after being exposed to high temperatures compared to the control samples.
Tipo
info:eu-repo/semantics/bachelorThesisDerechos
info:eu-repo/semantics/openAccessAttribution-NonCommercial-ShareAlike 4.0 International
Idioma
spaColecciones
El ítem tiene asociados los siguientes ficheros de licencia:
- Creative Commons
Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess