Comparación in vitro de la fuerza de adhesión de postes de fibra de vidrio con superficie tratada previo a su cementación con un agente resinoso autograbante
Average rating
Cast your vote
You can rate an item by clicking the amount of stars they wish to award to this item.
When enough users have cast their vote on this item, the average rating will also be shown.
Star rating
Your vote was cast
Thank you for your feedback
Thank you for your feedback
Issue Date
2018-01-23
Metadata
Show full item recordCitation
Sánchez Ríos, Fiorella; Torres Rivera, J. M. (2018). Comparación in vitro de la fuerza de adhesión de postes de fibra de vidrio con superficie tratada previo a su cementación con un agente resinoso autograbante. Universidad Peruana de Ciencias Aplicadas (UPC). Retrieved from http://hdl.handle.net/10757/622853Abstract
Objetivo: El presente estudio in vitro compara la fuerza de adhesión de los postes de fibra de vidrio tratados con distintos tratamientos de superficie antes de su cementación. Materiales y Métodos: Cuarenta piezas dentarias unirradiculares de bovino fueron cortadas obteniendo una raíz de 21 mm, que fueron endodonciadas y agrupadas en 4 grupos según el tratamiento de superficie del poste realizado posterior a la desobturación del conducto: Grupo 1 (Silano), Grupo 2 (Ácido Fosfórico, Silano), Grupo 3 (Peróxido de Hidrógeno, Silano) y Grupo 4 (Silano, Adhesivo); y la cementación de los postes de fibra según las especificaciones del agente resinoso empleado (RelyX U200 - 3M ESPE). Posterior a ello, las raíces fueron cortadas transversalmente con un grosor de 1 mm en una máquina de corte digital. Por último, se utilizó el test de push-out para medir la fuerza adhesiva. Resultados: La fuerza de adhesión de los grupos si evidenció diferencias en sus medianas (p=0.010). En las comparaciones por pares del Grupo 1 vs. Grupo 3, Grupo 1 vs. Grupo 4, Grupo 2 vs. Grupo 3, y Grupo 2 vs. Grupo 4 sí se encontraron diferencias estadísticamente significativas (p=0.010, p=0.004, p=0.009, p=0.019).Sin embargo, en las otras comparaciones por pares del Grupo 1 vs. Grupo 2, y Grupo 3 vs. Grupo 4, no se encontraron diferencias estadísticamente significativas (p=0.394 y p=0.387), donde el Grupo 3 y Grupo 4 tuvieron mayores fuerzas de adhesión (mediana de 3,49 Mpa y 4,13 Mpa respectivamente). Conclusiones: El tratamiento de superficie del poste de fibra de vidrio, con Peróxido de Hidrógeno con Silano, y Silano con Adhesivo obtuvo mejores resultados de fuerza adhesiva.Objective: This in vitro study compared the fiberglass posts bond strength treated with differents surface treatments before their cementation. Materials and Methods: Forty bovine teeth were seccionated in two, obtaining 21mm bovine roots. Bovine roots were endodontically treated and randomly divided into four groups according to the surface treatment of the post: Group 1 (Silane), Group 2 (Phosphoric Acid, Silane), Group 3 (Hydrogen Peroxide, Silane) and Group 4 (Silane, Adhesive). After that, the fiber posts were cemented with a resin agent (RelyX U200 - 3M ESPE), according manufacturer instructions and the samples were stored for 24 hours in distilled water at 37 °C. Roots were cut in slides in a digital cutting machine in order to obtain a 1 mm sample. Push out test was used to measure the bond strength at the speed of 0.5 mm/min. Results: The adhesion strength of the groups did show differences in their medians (p = 0.010). In the pairwise comparisons where it was using the Kruskal Wallis test, the (Group 1 vs. Group 3), (Group 1 vs. Group 4), (Group 2 vs. Group 3), and (Group 2 vs. Group 4) did found statistically significant differences (p = 0.010, p = 0.004, p = 0.009, p = 0.019).In the other pairwise comparisons using the posthoc of kruskall wallis test, the (Group 1 vs. Group 2), and (Group 3 vs. Group 4), were no found statistically significant differences (p = 0.394 and p = 0.387),so the Group 3 and Group 4 had higher adhesion forces (median of 3.49 MPa and 4.13 MPa respectively). Conclusion: The surface treatment of the fiberglass post, with Hydrogen Peroxide with Silane, and Silane with Adhesive obtained better results of adhesive strength.
Type
info:eu-repo/semantics/bachelorThesisRights